Alucoworld Acetic General Purpose / Silicone Sealant | ||||
Performance | Standard | Measured Value | Testing Method | |
Test at 50±5% RH and temperature 23±20C: | ||||
Density (g/cm3) | ±0.1 | 0.94 | GB/T 13477 | |
Tack-Free Time (min) | ≤180 | 10 | GB/T 13477 | |
Extrusion (ml/min) | ≥80 | 3750 | GB/T 13477 | |
Tensile Modulus (Mpa) | 230C | 0.4 | 0.1-0.4 | GB/T 13477 |
200C | or 0.6 | 0.1-0.6 | ||
Slumpability (mm) vertical | not change shape | not change shape | GB/T 13477 | |
Slumpability (mm) horizontal | ≤3 | 0 | GB/T 13477 | |
Curing Speed (mm/d) | 2 | 3 | / | |
As Cured -After 21 days at 50±5% RH and temperature 23±20C: | ||||
Hardness (Shore A) | 20~60 | 22 | GB/T 531 | |
Tensile Strength under Standard Conditions (Mpa) | / | 0.26 | GB/T 13477 | |
Elongation of Rupture (%) | / | 485.96 | GB/T 13477 | |
Movement Capability (%) | 12.5 | 12.5 | GB/T 13477 | |
Storage | 12 Months |
Directions for use
1. Ensure all surfaces are clean, dry ad grease-free. Remove all grit, oil, grease, detergents, flaking paint, any loose materials and old sealant.
2. Cut off tip of nozzle and cartridge. Screw on nozzle to cartridge.
3. Fit into chalking gun, applyn surface in steady flow.
4. If required smooth and shape sealant with spatula dipped in mild detergent.
5. Remove excess uncured sealant with a mineral turpentine soaked cloth. Fully cured excess sealant an be removed by trimming with a sharp knife.